C.G261.A70.B.3

A soft, black SEBS based thermoplastic elastomer (TPE) compound that contains PIR material and offers high temperature resistance and excellent compression set with superior UV resistance.

Processing Method: Extrusion, Injection Molding

Key Features

Recycled Raw Material Content
Reduced CO2 Emissions
Designed for Weatherseals
Enhanced Surface Quality
Excellent Weathering Resistance
Excellent Elastic Recovery
Adhesion to PP and PE

Typical Applications

Automotive Weatherseals

Regulations & Approvals

Physical Properties

Property

Typical Value (English)

Typical Value (SI)

Test Method

Density

1,10 g/cm3

ASTM D792

Durometer Hardness, 3 sec (Shore A)

ASTM D2240

Durometer Hardness, 3 sec (Shore D)

ASTM D2240

Tensile Strength at Break

798 Psi

5,50 MPa

ASTM D412, Method A

Mod. of %100 Elasticity

305 Psi

2,10 MPa

ASTM D412, Method A

Mod. of %300 Elasticity

566 Psi

3,90 MPa

ASTM D412, Method A

Elongation at break(%)

600 %

ASTM D412, Method A

Tear Resistance

154 lbf/in

27 N/mm

ASTM D624

Compression set (at 23⁰C, 73.40⁰F, 22h)

ASTM D395, Type 2, Method B

Compression set (at 70⁰C, 158⁰F, 22h)

ASTM D395, Type 2, Method B

Compression set (at 100⁰C, 212⁰F, 22h)

ASTM D395, Type 2, Method B

Compression set (at 125⁰C, 257⁰F, 72h)

ASTM D395, Type 2, Method B

Shrinkage (Flow)

ASTM D955

Shrinkage (Across Flow)

ASTM D955

The values presenter in this document apply only to the product mentioned above and cannot be extended to other products in general. Elastron is not responsible for the results that may arise from tests outside the control of Elastron. Although Elastron bases the information and suggestions contained herein on reliable data, it does not guarantee that such information and suggestions are correct, and that the product is suitable for its intended use.